Neodymium Rare Earth Magnets
Rods
Standard magnet characteristics
|
| All Rare Earth Magnets
are SILVER, any image variation is due to monitor, or photo
interpretation. |
| Magnetic Properties |
Magnetization Direction:
Axially Magnetised |
Size: D & T
Diameter & Thickness |
Temperature Range:
- 196°C / + 80°C
More |
 |
 |
 |
 |
|
|
Diameter:
3mm |
Diameter:
3mm |
Diameter:
3mm |
Diameter:
3mm |
|
Thickness:
3mm |
Thickness:
4mm |
Thickness:
10mm |
Thickness:
15mm |
|
Gauss:
3,700 |
Gauss:
2,500 |
Gauss:
3,200 |
Gauss:
3,600 |
|
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
|
Pull Strength:
270g |
Pull Strength:
299g |
Pull Strength:
358g |
Pull Strength:
375g |
|
Weight:
1 grams |
Weight:
1 grams |
Weight:
2 grams |
Weight:
3 grams |
 |
|
 |
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added to the purchase price at Check Out |
|
|
Diameter:
4mm |
Diameter:
4mm |
Diameter:
5mm |
Diameter:
6mm |
|
Thickness:
5mm |
Thickness:
20mm |
Thickness:
10mm |
Thickness:
6mm |
|
Gauss:
3,000 |
Gauss:
3,600 |
Gauss:
4,500 |
Gauss:
4,500 |
|
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
|
Pull Strength:
612g |
Pull Strength:
712g |
Pull Strength:
1,000g |
Pull Strength:
1,350g |
|
Weight:
1 grams |
Weight:
2 grams |
Weight:
3 grams |
Weight:
2 grams |
 |
 |
 |
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added
to the purchase price at Check Out |
|
|
Diameter:
6mm |
Diameter:
6mm |
Diameter:
8mm |
Diameter:
8mm |
|
Thickness:
15mm |
Thickness:
25mm |
Thickness:
8mm |
Thickness:
25mm |
|
Gauss:
4,800 |
Gauss:
4,800 |
Gauss:
4,900 |
Gauss:
5,700 |
|
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
|
Pull Strength:
1,600g |
Pull Strength:
1,600g |
Pull Strength:
3,000g |
Pull Strength:
3,000g |
|
Weight:
4 grams |
Weight:
6 grams |
Weight:
4 grams |
Weight:
10 grams |
 |
 |
 |
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added
to the purchase price at Check Out |
|
|
Diameter:
8mm |
Diameter:
10mm |
Diameter:
10mm |
Diameter:
10mm |
|
Thickness:
30mm |
Thickness:
10mm |
Thickness:
12mm |
Thickness:
16mm |
|
Gauss:
5,500 |
Gauss:
4,800 |
Gauss:
5,100 |
Gauss:
5,200 |
|
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
|
Pull Strength:
3,000g |
Pull Strength:
4,000g |
Pull Strength:
4,200g |
Pull Strength:
4,300g |
|
Weight:
12 grams |
Weight:
6 grams |
Weight:
8 grams |
Weight:
9 grams |
|
|
 |
 |
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added
to the purchase price at Check Out |
|
|
Diameter:
10mm |
Diameter:
10mm |
Diameter:
15mm |
Diameter:
20mm |
|
Thickness:
20mm |
Thickness:
50mm |
Thickness:
30mm |
Thickness:
20mm |
|
Gauss:
5,400 |
Gauss:
5,500 |
Gauss:
5,500 |
Gauss:
5,850 |
|
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
Grade:
N42 |
|
Pull Strength:
4,500g |
Pull Strength:
4,700g |
Pull Strength:
11,000g |
Pull Strength:
16,000g |
|
Weight:
12 grams |
Weight:
30 grams |
Weight:
50 grams |
Weight:
50 grams |
|
|
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added
to the purchase price at Check Out |
|
|
Diameter:
25mm |
Diameter:
40mm |
Diameter:
50.80mm |
|
|
Thickness:
25mm |
Thickness:
40mm |
Thickness:
50.80mm |
|
|
Gauss:
5,600 |
Gauss:
5,950 |
Gauss:
6,250 |
|
|
Grade:
N42 |
|
|
|
|
Pull Strength:
26,700g |
Pull Strength:
75,000g |
Pull Strength:
138,000g |
|
|
Weight:
110 grams |
Weight:
410 grams |
Weight:
1100 grams |
|
|
|
 |
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| All Australian purchases will have GST added
to the purchase price at Check Out |
|
| Rare Earth Discs -
Rods -
Blocks -
Rings -
PK Rings -
Shallow Pots -
Pots & Hooks -
Pots & BOS |
|
Pots & Eyelets -
Pots Rubber Coated -
Rare Earth Spheres -
Fishing Magnets |
| Rods are determined as having the same thickness
or greater than the diameter of the magnet. |
| |
Contact Fastmag to quote on bulk purchases |
| |
|
|
Pull Strength |
 |
|
The Pull Force is the force required to pull a magnet
free from a flat steel plate using force perpendicular
to the surface. This is the standard for testing
magnet pull strength. Air gaps and changes in surface
material will substantially reduce the effectiveness
of the pull force, or pull strength of the magnet.
|
|
|